Asphalt Waterproofing Membrane for Concrete Roof Repair

• Customization: Available
• After-sales Service: Provide
• Certification: CE, ISO
• Model NO.: HDPE
• Thickness: 0.8mm-4mm
• Raw Material: Bitumen
• Type: Waterproof Roll Material
• Ceiling Tile Shape: Roll
• Function: Anti-Static, Waterproof
• Color: Black
• Usage: Outdoor, Indoor
• Warranty: 1 Years
• Material: Bitumen
• Ceiling Tile Type: None
• Surface Treatment: None
• Transport Package: in Roll
• Specification: 3mm - 5mm
• Trademark: Jubo
• Origin: Jiangxi, China
• HS Code: 3918109000
• Production Capacity: 5000 Square Meter/Week
• Package Size: 10.00cm * 10.00cm * 0.30cm
• Package Gross Weight: 1.000kg

Product Description

Waterproof High Polymer HDPE Self Adhesive Bitumen Waterproof membrane
 

Product Description

APPLICATION
SBS/APP modified bitumen membrane is used as waterproofing/damp proofing membrane for protection of various substrates in wide
range of applications which included the following:
• Roofs
• Terraces, balconies & patios
• Sunken slabs
• Concrete foundations & footings
• Basements
• Pile heads
• Bridges & tunnels
• Airport aprons & ramp areas

ADVANTAGES
• High resistance to positive water & vapor pressure
• Good dimensional stability under tension
• Excellent flexibility
• High puncture and fatigue resistance
• High tensile and tear strengths
• Resists water borne chemicals
• Accommodates structural movement






Product  Specification:

SBS Executive Standard

Number	Item			I		II
				PY	G	PY	G	PYG
1	Soluble content (g/ m^2) ≥		3mm	2100				*
			4mm	2900				*
			5mm	3500
			Experimental phenomena	*	Tire base is not flammable	*	Tire base is not flammable	*
2	Heat resistance		ºC	90		105
			≤mm	2
			Experimental phenomena	No flowing, no dripping
3	Low temperature flexibility ºC			-20		-25
				No cracks
4	Impermeable 30min			0.3Mpa	0.2Mpa	0.3Mpa
5	pull	Max (N/50mm)		500	350	800	500	900
		Second (N/50mm)		*	*	*	*	800
		Experimental phenomena		Stretching process, the middle part of the test piece without bitumen coating cracking or separation with the tire base
6	Elongation rate	Max %≥		30	*	40	*	*
		Second %≥		*		*		15
7	Oil permeability			Number of sheets≤	2

Performance Index Of Tese Report
S/N	Item		Index
			I		II
			PY	G	PY	G	PYG
1	Soluble content	≥3mm g/m^2	≥2100 g/m^2				/
		≥4mm g/m^2	≥2900 g/m^2				/
		≥5mm g/m^2	≥3500 g/m^2
		Tese results	-	Reinforced layer Nonflammable	-	Reinforced layer Nonflammable	-
2	Heat resistance		110ºC		130ºC
			≤2mm
			No flow, no dripping
3	Low temperature flexibility		-7ºC		-15ºC
			No crack
4	Impermeable(120min)		0.3Mpa	0.2Mpa	0.3Mpa
5	Pulling	Maximum peak tension	≥500N/50mm	≥350N/50mm	≥800N/50mm	≥500N/50mm	≥900N/50mm
		Sub-peak peak tension	-	-	-	-	≥800N/50mm
		Test results	During the tensile process, there is no craking of the membrane upper cover layer or the separation of the reinforced layer in the middle of the test piece
6	Elongation rate	Maximum peak elongation	≥25%	-	≥40%	-	-
		Second peak elonagation	-		-		≥15%
7	Increased quality after soaking	PE/S	1.0
		M	≤2.0%
8	Thermal aging	Rally retention rate	≥90%
		Elongation retention rate	≥80%
		Low temperature flexibility	-2ºC		-10ºC
			No crack
		Size change rate	≤0.7%	-	≤0.7%	-	≤0.3%
		Loss of quality	≤0.1%
9	Joint peel strength		≥1.0N/mm
10	Nail tear strength		-				≥300N
11	Mineral pellet adhesion		≤2.0g
12	The thickness of bitumen cover layer on the downward covered surface of the membrane		≥1.0mm
13	Artificial weather accelerated aging	Appearance	No sliding, flowing, dripping
		Rally retention rate	≥80%
		Low temperature flexibility	-2ºC		-10ºC
			No crack